Permeable paver and manufacturing method therefor

ABSTRACT

A permeable paver that has water permeability of on average about 1 inch per hour and compressive strength of an average of about 8000 psi, the paver manufactured by forming a mixture comprising blast-furnace slag, sand, gravel and portland cement into predetermined sizes, shapes and colors as desired utilizing a hydraulic-type or equivalent compacting block forming machine.

RELATED APPLICATION(S)

This application is a Continuation-In-Part Application of U.S. patent application Ser. No. 12/537,924 filed Aug. 7, 2009, now U.S. Pat. No. 7,927,037 entitled “PERMEABLE PAVER AND MANUFACTURING METHOD THEREFOR”, which is incorporated herein by reference in its entirety, and claims any and all benefits to which it is entitled therefrom. This Application is also related to PCT Patent Application No. PCT/US10/43415 filed Jul. 27, 2010 entitled “PERMEABLE PAVER AND MANUFACTURING METHOD THEREFOR”, which is also incorporated herein by reference in its entirety, and claims any and all benefits to which it is entitled therefrom.

FIELD OF THE INVENTION

This invention relates to permeable pavers and their method of manufacturing, and more particularly to porous pavers and paving stones manufactured using recycled materials and other green technologies that allow moisture to permeate and drain therethrough.

BACKGROUND OF THE INVENTION

Slag has many commercial uses, and is rarely discarded. It is often reprocessed to separate any other metals that it may contain. The remnants of this recovery can be used in railroad track ballast and as fertilizer. It has been used as a road base material and as a cheap and durable means of roughening sloping faces of seawalls to progressively arrest the movement of waves. Blocks of slag have been used in the construction of retaining walls and foundations.

What was once an unwanted by-product of the steel making process can now be recycled and used in the manufacture of high performance concretes. When iron ore is heated in a blast furnace the impurities or ‘slag’, which include large quantities of calcium and silica, become molten and are separated from the raw iron.

As the slag is channeled out of the furnace, thousands of gallons of water are poured over it. This rapid cooling, often from a temperature of around 2,600° C., is the start of the granulating process. This process causes several chemical reactions to take place within the material, and gives the slag its cementitious properties.

The water carries the slag in its slurry format to a large agitation tank from where it is pumped along a piping system into a number of gravel based filter beds. The filter beds then retain the slag granules while the water filters away and is returned to the system.

When the filtering process is complete, the remaining slag granules, which now give the appearance of coarse beach sand, can be scooped out of the filter bed and transferred to the grinding facility where they are ground into particles that are finer than portland cement

This previously unwanted recycled product is used in the manufacture of high performance concretes, especially those used in the construction of bridges and coastal features where its low permeability and greater resistance to chlorides and sulfates can help to reduce corrosive action and deterioration of the structure.

An interlocking paver is a pre-cast piece of concrete or brick commonly used as an alternative to plain concrete or asphalt or other paving materials. Pavers can be assembled to cover walkways, patios, pool decks and driveways and airport or loading docks. Interlocking pavers are available in a wide range of shapes such as rectangular, hexagonal, etc. and each allows them to be jointed fittingly to create a paving surface. The advantage of using interlocking pavers over the asphalt and poured concrete are high compressive strengths which can reach 7000+psi, pleasant look, time saving, easy removal and relaying etc.

There are quite a few traditional interlocking pavers available in the market. They are available in different shapes, sizes and made of different materials. Common building materials are concrete and clay, and by adapting different manufacturing methods pavers of various physical properties can be achieved. For example, pressing the dry concrete-mix into molds rather than pouring a wetter mix results in their 8000+psi compressive strength, making concrete paving stones a more durable choice than clay bricks or poured-in-place concrete. Clay pavers have an advantage with resistance to fading from the sun and deterioration from long term exposure to the elements. Because clay pavers are fired, the pores of the paver are at least partially vitrified closed, therefore creating an almost non-permeable surface. Another disadvantage of clay pavers is lack of choice of color spectrum. Clay pavers are formed from a natural material, so the feasible range of colors is more limited. Concrete, in contrast, has an essentially limitless color spectrum when starting with white portland cement and using pigments.

Installation of interlocking pavers starts with a compacted stone sub-base and a leveling bed of sand, pavers of desirable size, shape and material. Instead of connecting the pavers by pouring grout between the joints, as one would with tiles, sand particles are spread over the pavers and tamped down. The sand stabilizes the interlocking pavers yet allows for some flexibility. This type of pavement will absorb stress such as small earthquakes, freezes and thaws, and slight ground erosion by shifting each paver slightly. Therefore they are less likely to crack or buckle like poured cement.

Due to the increasing environment concerns, however, there has been a upward demand on permeable paving materials, which provide water permeable properties as well as strength for use as paving materials. Permeable paving materials allow moisture to filter through and replenish underground water tables and other water sources. It also helps to drain water into the ground and relieve stress on over taxed storm water systems during high rain conditions.

In the past, concrete pavers have contributed to the LEED (“Green Building”) rating system. Originally developed for the U.S. Department of Energy and standing for Leadership in Energy and Environmental Design, LEED is growing in use by design professionals in response to federal, state, and local government agencies, and by private developers. LEED uses a point rating system to recognize sustainable site and building design. Depending upon geographical location due to varying enabling legislation and practice in the different states, complying with the rating system is voluntary and it aims to improve environmental and economic performance of buildings and sites. Developed by consensus with the participation of many organizations, the rating system and certification program based on providing evidence of compliance to the rating system is administered by the U.S. Green Building Council. A complete description and downloads can be found on the Internet at www.usgbc.org/LEED.

Importantly, concrete pavers and permeable interlocking concrete pavers can earn points or “credits” in the LEED rating system. Credits are earned under several categories of use including stormwater management, local/regional materials, and exterior design to reduce heat islands. For stormwater management, Credit 6.1 (1 point) can be earned for building sites where the existing impervious area is greater than 50%. Permeable interlocking concrete pavement can meet this requirement. In some urbanized areas with this extent of impervious cover, permeable interlocking concrete pavement may be more cost-effective than separate water detention and/or retention facilities due to space and configuration constraints. The LEED requirement is that runoff rate and quantity be reduced by at least 25%. In the past, permeable interlocking concrete pavements have been able to reduce runoff to zero for the most frequent storms.

Credit 6.2 provides 1 point for treatment systems designed to remove 80% of the average annual post development total suspended solids (TSS), and 40% of the average annual post development total phosphorus (TP). The ability of permeable interlocking concrete pavements to reduce these pollutants is typically greater than these percentages according to references in the Interlocking Concrete Pavement Institute's manual, Permeable Interlocking Concrete Pavements—Selection, Design, Construction, Maintenance. The ICPI manual references studies on infiltration trenches (similar to permeable pavement bases) and porous pavements with reductions in TSS as high as 95% and TP as much as 70%.

Another source of credit is designated as Credit 5 (1 to 2 points), local regional materials: specify a minimum of 20% of building materials that are manufactured regionally within a radius of 800 km (500 miles). An additional point is earned if 50% of the regionally manufactured materials are extracted, harvested or recovered within this same radius. Most interlocking concrete pavers and permeable pavers will be manufactured within this distance from the project site.

Yet another Credit is 7.1 (1 point), landscape and exterior design to reduce heat islands. An option for meeting this requirement is to use light colored/high albedo materials with a reflectance of at least 0.3 for 30% of the sites non-roof impervious surfaces, i.e., pavements. Concrete paving units can be manufactured in practically any color, so they can be tailored to register an albedo of at least 0.3.

Albedo is defined as the ratio of outbound or reflected solar radiation to inbound radiation. It is measured with a pyranometer. A pyranometer is a type of actinometer used to measure broadband solar irradiance on a planar surface and is a sensor that is designed to measure the solar radiation flux density in watts per square meter from a field of view of 180 degrees. The name pyranometer stems from Greek, “pyr” meaning “fire” and “ano” meaning “above” or “sky”. A typical pyranometer does not require auxiliary power to operate. Long-term measurements should be done with two pyranometers rather than one to better understand and compare diurnal changes in the radiation flux of pavements.

U.S. Pat. No. 6,419,740, issued Jul. 16, 2002 to Kinari et al. teaches a water-permeable solid material which can be used as paving materials. However, the materials are not and cannot be made into paver form. U.S. Pat. No. 6,824,605, issue Nov. 30, 2004 to De Buen-Unna, et al. also teaches ecological permeable concretes with high compression, bending and abrasion resistance for paving purposes, but again, the materials are not made into a paver form.

The American Concrete Institute defines a Supplementary Cementitious Material (SCM) as an “inorganic material such as fly ash, silica fume, metakaolin, or ground-granulated blast-furnace slag that reacts pozzolanically or hydraulically.” A material that reacts with by-products of the portland cement reaction to form additional binder material is a pozzolan. SCMs including fly ash and ground-granulated blast-furnace slag are often used to replace portland cement. Other SCMs, such as silica fume and other high silica content materials, are used to enhance various properties of concrete.

Processes for producing SCMs include mineralization via aqueous precipitation are known. FIG. 1A (Prior Art) shows one such process which utilizes carbon dioxide and other pollutants such as sulfur dioxide, fly ash, salt and other manufacturing process brines, waste water and sodium hydroxide to produce calcium carbonates, other green building materials and clean flue gas. Carbon dioxide from waste flue gas, such as that produced by typical energy plants which burn coal or other organic compounds, is converted into stable or metastable, solid calcium and magnesium carbonate and bicarbonate minerals, similar to those found in the skeletons of marine animals and plants. Typical mineralization via aqueous precipitation involves contacting flue gas from the power plant with natural waters found in abundance on Earth. Many of the crystallographic forms synthesized utilizing these processes make it possible to produce high reactive cements.

Unfortunately, prior uses of SCMs to replace portland cement in typical concrete have been unable to produce building materials having compressive strengths greater than 8000 psi using testing under ASTM C 1157 “Standard Performance Specification for Hydraulic Cement”. FIG. 1B (Prior Art) shows the results of testing done in accordance with ASTM C 109. This data shows that SCMs produce compressive strengths similar to portland cement at up to a 20% replacement of portland cement. These compressive strengths of between 2000 and 6000 psi are insufficient for use as paving stones in which compressive strengths of 8000+psi are required.

A carbon credit is a generic term for any tradable certificate or permit representing the right to emit one tonne of carbon or carbon dioxide equivalent (tCO₂e). Carbon credits and carbon markets are a component of national and international attempts to mitigate the growth in concentrations of greenhouse gases (GHGs). One carbon credit is equal to one ton of carbon dioxide, or in some markets, carbon dioxide equivalent gases. Carbon trading is an application of an emissions trading approach. Greenhouse gas emissions are capped and then markets are used to allocate the emissions among the group of regulated sources. The goal is to allow market mechanisms to drive industrial and commercial processes in the direction of low emissions or less carbon intensive approaches than those used when there is no cost to emitting carbon dioxide and other GHGs into the atmosphere. Since GHG mitigation projects generate credits, this approach can be used to finance carbon reduction schemes between trading partners and around the world.

A carbon offset is a reduction in emissions of carbon dioxide or greenhouse gases made in order to compensate for or to offset an emission made elsewhere. Carbon offsets are measured in metric tons of carbon dioxide-equivalent (CO₂e) and may represent six primary categories of greenhouse gases. One carbon offset represents the reduction of one metric ton of carbon dioxide or its equivalent in other greenhouse gases.

There are two markets for carbon offsets. In the larger, compliance market, companies, governments, or other entities buy carbon offsets in order to comply with caps on the total amount of carbon dioxide they are allowed to emit. This market exists in order to achieve compliance with obligations of Annex 1 Parties under the Kyoto Protocol, and of liable entities under the EU Emissions Trading Scheme. In 2006, about $5.5 billion of carbon offsets were purchased in the compliance market, representing about 1.6 billion metric tons of CO₂e reductions. In the much smaller, voluntary market, individuals, companies, or governments purchase carbon offsets to mitigate their own greenhouse gas emissions from transportation, electricity use, and other sources. For example, an individual might purchase carbon offsets to compensate for the greenhouse gas emissions caused by personal air travel. Many companies offer carbon offsets as an up-sell during the sales process so that customers can mitigate the emissions related with their product or service purchase, such as offsetting emissions related to a vacation flight, car rental, hotel stay, consumer good, etc. In 2008, about $705 million of carbon offsets were purchased in the voluntary market, representing about 123.4 million metric tons of CO₂e reductions. Offsets are typically achieved through financial support of projects that reduce the emission of greenhouse gases in the short- or long-term. The most common project type is renewable energy, such as wind farms, biomass energy, or hydroelectric dams. Others include energy efficiency projects, the destruction of industrial pollutants or agricultural byproducts, destruction of landfill methane, and forestry projects. Some of the most popular carbon offset projects from a corporate perspective are energy efficiency and wind turbine projects.

ADVANTAGES AND SUMMARY OF THE INVENTION

The present invention is a paver that has good water permeability and yet strength for use as a paving material. It combines all the advantages of pavers and water-permeable concrete materials and provides an ideal paving material both for indoor and outdoor installations.

One advantage and object of the present invention is the easiness of installation and removal. The mere special tools needed for installing interlocking pavers are vibrating compaction machine or “Vibra Plate” and Shear Cutter. The former is used to compact the base material to 90% density minimum and also to set and interlock the pavers into the sand bed. The latter is used to cut the pieces to fit at corners and edges. The sand does not easily wash out with rain or garden hose water. Since all pavers are ready to be used, no on the spot formulating or mixing of concrete is required.

Another advantage and object of the present invention is to provide a paving material with high compressive strengths of up to 7000+psi as per BS and 8000+psi as per ASTM codes and standards.

Yet another advantage and object of the present invention is to provide environmentally-friendly building materials. Rain water and moisture can permeate and pass through the present invention and reach subterranean water tables. This helps replenish underground water sources and also solves drainage problems in urban as well as rural areas.

Another advantage and object of the present invention is to provide a paving material in compliance with LEED standards and guidelines. In the present case, the present invention is useful for preventing run-off of rain or storm water. As rainwater is absorbed, pollutants are also filtered and removed from the water, thus avoiding the need for storm water collection, retention and treatment facilities. The present invention is also useful for increasing reflectance of solar energy, thus preventing “heat islands” from developing which would alter the environmental impact of development. Due to the ready availability of the materials of construction and ability to utilize existing equipment for manufacturing, the permeable pavers of the present invention can be made and distributed locally.

Yet another advantage and object of the present invention is the aesthetic factors. With the variety of shapes, colors and assembly orientations, designers/installers can easily create a pattern on any surface which is difficult for asphalt and poured cement.

It is yet a further advantage of the present invention to incorporate Supplementary Cementitious Materials [hereafter SCMs] manufactured utilizing technology which reduces carbon emissions. Mineralization of calcium carbonates via aqueous precipitation can provide enhanced savings in terms of carbon credits and/or carbon offsets which offset the cost of recovery of these materials.

Further details, objects and advantages of the present invention will become apparent through the following descriptions, and will be included and incorporated herein.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a representative flow diagram illustrating the production process of environmental friendly SCMs.

FIG. 1B is a chart showing the results of testing done in accordance with ASTM C 109.

FIG. 2 is a flowchart showing the steps of manufacturing permeable paver 100 of the present invention.

FIG. 3 is a representative drawing showing possible sizes and shapes for permeable pavers 100 of the present invention.

FIG. 4 is a chart showing experimental test results of water flow rate through the permeable paver 100 of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

The description that follows is presented to enable one skilled in the art to make and use the present invention, and is provided in the context of a particular application and its requirements. Various modifications to the disclosed embodiments will be apparent to those skilled in the art, and the general principals discussed below may be applied to other embodiments and applications without departing from the scope and spirit of the invention. Therefore, the invention is not intended to be limited to the embodiments disclosed, but the invention is to be given the largest possible scope which is consistent with the principals and features described herein.

It will be understood that in the event parts of different embodiments have similar functions or uses, they may have been given similar or identical reference numerals and descriptions. It will be understood that such duplication of reference numerals is intended solely for efficiency and ease of understanding the present invention, and are not to be construed as limiting in any way, or as implying that the various embodiments themselves are identical.

FIG. 2 is a flowchart showing the steps of manufacturing permeable paver 100 of the present invention. In Step 102, the process starts off as the Batch Computer receives an order to make a load of permeable paver 100.

In Step 104, raw materials that consist of blast slag, sand, gravel, optionally a color agent, cement and water are pre weighed according to the order quantity, desired physical properties and shapes of permeable paver 100.

The following table shows experimentally utilized mix design test formulae for the permeable paver 100 of the present invention.

TABLE 1 Mix Design for Permeable Paver 100 Value in kg 20% Mix Design (¼ gravel) 25% 30% 35% 40% 45% 50% 15% (Cement) Slag 600 600 600 600 600 600 600 ¼ gravel 160 200 240 280 320 360 400 Sand 200 200 200 200 200 200 200 Cement 144 150 156 162 168 174 180 16% Slag 600 600 600 600 600 600 600 ¼ gravel 160 200 240 280 320 360 400 Sand 200 200 200 200 200 200 200 Cement 153.6 160 166.4 172.8 179.2 185.6 192 17% Slag 600 600 600 600 600 600 600 ¼ gravel 160 200 240 280 320 360 400 Sand 200 200 200 200 200 200 200 Cement 163.2 170 176.8 183.6 190.4 197.2 204 18% Slag 600 600 600 600 600 600 600 ¼ gravel 160 200 240 280 320 360 400 Sand 200 200 200 200 200 200 200 Cement 172.8 180 187.7 194.4 201.6 208.8 216 19% Slag 600 600 600 600 600 600 600 ¼ gravel 160 200 240 280 320 360 400 Sand 200 200 200 200 200 200 200 Cement 182.4 190 197.6 205.2 212.8 220.4 228 20% (Cement) Slag 600 600 600 600 600 600 600 ¼ gravel 160 200 240 280 320 360 400 Sand 200 200 200 200 200 200 200 Cement 192 200 208 216 224 323 240 21% Slag 600 600 600 600 600 600 600 ¼ gravel 160 200 240 280 320 360 400 Sand 200 200 200 200 200 200 200 Cement 201.6 210 218.4 226.8 235.2 243.6 252

Materials:

The following materials may be used and are presented here as examples only. Slag: Granulated Blast-Furnace Slag (GGBFS), which has been sieved to remove particles larger than 3/16″ with sieve size #4; ¼″ Gravel: Crystalline Silica (Aggregate); and Cement: Permanent Type 1-2-3-5; and white cement.

Supplementing the formulae or process for manufacturing the permeable pavers of the present invention can provide control over permeability. It will be understood that while materials including addmix and fly ash are commonly used with concrete objects, their use in the permeable pavers of the present invention will provide the manufacturers with a tool for limiting or decreasing permeability, in the event of, for example, a level, uniform, maximum 1″ per hour rate of water permeation is desired. It will be understood, however, that there will be a limiting factor on the permeability of the pavers 100 of the present invention through use of these materials.

Thus, the pavers of the present invention are composed of (i) a base of 3 parts by weight of slag and 1 part by weight of sand, (ii) between about 20% and about 50% by weight of gravel, and (iii) between about 15% and about 21% portland-type or equivalent cement. These formulations are best suited for preparation of a paver 100 of the present invention having break strength of minimum 8000 psi, the ASTM requirement for building pavers. Moreover, permeability of the present paver 100 is greater than 1″ per hour, and the LEED standard requires at least 1″ per hour permeability. To determine the entire volume of water flow through the permeable pavers 100, the area of the paver can be used to determine the overall volumetric flow through the paver.

In one alternative embodiment, calcium carbonate precipitate powder such as that manufactured by Calera Corporation at their Moss Landing, Calif. facility, is used to replace part of the portland-type or equivalent cement in previous formulae of the permeable pavers 100′. In one embodiment, precipitate powder manufactured utilizing a mineralization via aqueous precipitation process can replace 10%-40% by weight of the portland type or equivalent cement in the formulae of the permeable pavers 100′. In one embodiment, approximately 30% by weight SCM in the form of precipitate powder strikes a balance between functionality in terms of permeability and strength of the permeable paver 100′ and the environmental benefits of carbon reduction. Utilizing SCMs produced by mineralization via aqueous precipitation is able to reduce carbon emissions from CO₂-producing processes.

Detailed information for calcium carbonate precipitate powder such as found in the typical Material Safety Data Sheet follows:

-   Product name: Precipitate powder -   Composition/Information on Ingredients:

Estimated Composition

Sodium salts >20%  Magnesium/Calcium hydroxide >5% CalciumiSodiurn/ >5% Magnesiurn carbonates Water <1%

Hazards Identification

-   Appearance: White powder -   Effects of acute exposure: -   Eyes: Can irritate eyes -   Skin: Can dry and irritate skin -   Inhalation: Can cause coughing and respiratory tract irritation in     dry form -   Ingestion: Possible but unlikely to occur in large quantities -   Carcinogenicity: No information found -   Medical conditions aggravated: May aggravate any pre-existing     chronic respiratory disease in dry form

First-Aid Measures

-   Eye contact: Flush eyes with copious amounts of water for at least     15 mm Assure adequate flushing of eyes by separating eyelids with     fingers. Obtain medical attention. -   Skin contact: Flush skin with copious amounts of water for at least     15 mm, while removing contaminated clothing and shoes, ‘Nash     contaminated clothing before reuse. Call physician if irritation     develops. -   Inhalation: Remove to fresh air. If breathing is difficult, give     oxygen and seek medical attention. -   Ingestion: If swallowed, wash out mouth with water, provided person     is conscious. Do not induce vomiting. Obtain medical attention     immediately.

Firefighting Measures

-   Stability: Product is considered stable. -   Flash point and method: Non flammable. -   Extinguishing media: Use appropriate media to control primary source     of fire. Otherwise, use dry chemical, carbon dioxide, water spray or     foam. -   Hazardous combustion products: Decomposition products are unknown     and are not suspected. -   Firefighting instructions: No special procedures:

Accidental Release Measures

-   Spill/leak procedures: Vacuum powder and wet sweep to avoid dust     dispersal. Rinse area with water. -   Personal precautions: Use personal protective equipment: gloves,     safety glasses, and protective clothing -   Environmental precautions: No ecological problems are to be expected

Handling and Storage

-   Safe handling advice: Use personal protective equipment as described     in Accidental Release Measures section. Always wash hands after     handling the product and before eating or drinking. -   Storage conditions: Store in a cool, dry place in a tightly closed     container. -   Incompatible products: Unknown

Exposure Control/Personal Protection

-   Personal protective equipment: -   Respiratory protection: Use NIOSH/MSHA approved respirators if     ventilation is not adequate. -   Hand protection: Gloves -   Eye protection: Safety glasses -   Skin and body protection: Long-sleeve protective clothing -   Specific hygiene measures: Wash hands afterworking with substance.     Change contaminated clothing.

Physical and Chemical Properties

-   Molecular weight: Mixture -   Physical state: Powder -   Form and color: Whitish -   Odor: None -   pH: 8.0-11.0 -   Boiling point/range: No data available -   Melting point/range: Not applicable to liquid. No data for solid. -   Decomposition temperature: No data available -   Flashpoint: Not flammable. -   Autoigntion temperature: Not flammable -   Flammability limits: No data available. -   Freeze point: No data available -   Vapor pressure: No data available -   Vapor density: No data available -   Density (bulk): No data available -   Solubility in water: No data available

Stability and Reactivity

-   Conditions to avoid: Keep bottle closed until use -   Materials to avoid: Unknown -   Hazardous decomposition products: Decomposition products are unknown     and are not suspected

Toxicological Information

Effects of acute exposure:

-   Skin: Can cause irritation or rash on contact with abraded skin -   Eyes: Can cause irritation -   Nose: Inhalation of dust can cause nose, throat, and respiratory     tract irritation and coughing

Ecological Information

No data available.

Disposal Considerations

The material can be disposed in a permitted landfill in accordance with applicable federal, state, and local rules.

Transportation Information

Not regulated.

Regulatory Information

Not regulated.

In Step 106, when all raw materials are weighed and ready, blast slag, sand and gravel will be poured into the mixer, followed by cement, optionally a color agent, and water. The mixing time is approximately 3 minutes. Water is added to attain desirable consistency of the entire mixture and the amount of water used depends upon humidity during the mixing process. Coloring and pigmentation is added as desired.

In Step 108, the mixture in the mixer is discharged onto a conveyor to the block machine hopper. The hopper opens loading filling box. The filling box will then travels over the mold for permeable paver 100, filling the entire internal chamber of the mold with or without vibration/shaking.

In Step 110, the tamper head comes down to pressure the mixture inside the mold with approximately 30 bars pressure and the mold with vibration lasting for about 2 seconds.

In Step 112, the mold rises as the tamper head pushes the permeable paver 100 down onto a production board. The production board is then pushed onto a conveyor and accumulated onto the inlet elevator.

In Step 114, the inlet elevator fills and the finger car picks up the batch of permeable pavers 100 and moves to the drying racks.

In Step 116, the finger car then transfers a cured load of permeable paver 100, to the outlet elevator.

In Step 118, the production boards are conveyed to the cuber. Therein they will pick up the batch of permeable pavers 100 and move it onto a pallet for bagging and shipping.

In Step 120, the now empty production boards will return to the block machine and the process ends.

Equipment useful for manufacturing the pavers of the present invention is known and existing. As an example equipment manufactured by KVM International in Denmark, located online at www.KVM.com for the precast concrete industry are particularly well suited for manufacturing the permeable pavers of the present invention. Block forming machines are known in the prior art and will be incorporated herein by reference. As an example, the catalog entitled Machines for the Precast Concrete Industry regarding equipment manufactured by KVM International includes equipment including but not limited to Blockmachine, Series I Type 62/62, Blockmachine, Series I Type 62/80 and 62/97, Blockmachine, Series II Type 62/105, 90/105 and 62/125, Blockmachine, Series III Type 80/125, 105/125, 125/125, Control for Blockmachines PLC/PC, version 3, Cubing Systems Type M80/120, H120, HS 140 and associated Handling Systems.

A typical cement that can be used is manufactured by Lehigh Portland Cement Company under product name ALLCEM CEMENT. Material Safety Data Sheet describes the components of the cement as having about 30-45% hydrated amorphous silica, about 30-45% calcium compounds, about 8-15% magnesium compounds, about 5-15% aluminum compounds, about 0-4% sulfur, about 0-1% of the following: iron, titanium, manganese and potassium compounds, and about 0-0.2% crystalline silica. Other cements manufacturers and types will be known to those skilled in the art.

Blast-furnace slags are well known. Ground granulated blast-furnace slag or equivalent can be used in the present invention.

FIG. 3 is a representative drawing showing the possible sizes and shapes for permeable pavers of the present invention. It will be understood that pavers can be formed having square or rectangular and trapezoidal or hexagonal or other multi-sided shapes. Additionally, pavers can be made to increase drainage by having spacer tabs or bars integrally formed therein, and can be interlocking or fitted together as desired. Various shapes and sizes will be known to those skilled in the art.

Experimental Test Results

FIG. 4 is a chart showing experimental test results of water flow rate through the permeable paver 100 of the present invention.

Test Set Up:

Permeable pavers 100 of the present invention are installed on a bed of sand/gravels, emulating the actual application. Edges of permeable pavers 100 are water sealed to each other and to the perimeter with silicon or other elastomeric and sealing material to ensure moisture is flowing through the pavers 100 themselves, and not around or through holes/gaps between them. A water collection tank of the exact same dimensions is placed directly underneath permeable pavers 100. Water is poured on top of the permeable pavers 100 continuously. Water starts to flow through permeable pavers 100 and is collected in the water collection tank. The total depth of water collected was then measured periodically over time, from 0 minutes to 180 minutes at a period of 10 minutes. The differences between consecutive measurements is equivalent to the amount of flow over the respective 10-minute period. The flow per hour during any given 10-minute period is then known. IT will be understood that by deleting a statistically few test data points due to their apparent error or otherwise unusual deviation from average, smoother data curves can be obtained. Other techniques for calculating and graphing smoothed averages will be known by those skilled in the art.

The following table shows experimentally obtained test results for the permeable paver 100 of the present invention.

TABLE 2 Experimental Test Results for Permeable Paver 100 Time lapse Water collected Flow rate (Minutes) (Inches) (Inches/hour) 0 0 0 10 0.5 3 20 0.5 3 30 0.25 1.5 40 0.5 3 50 0.15 0.9 60 0.1 0.6 70 0.2 1.2 80 0.3 1.8 90 0.25 1.5 100 0.05 0.3 110 0.2 1.2 120 0.25 1.5 130 0.25 1.5 140 0.2 1.2 150 0.2 1.2 160 0.15 0.9 170 0.2 1.2 180 0.25 1.5

As shown in FIG. 4, during the initial period the flow rate is irregular as water commences filling holes and pores in the permeable pavers 100. After permeable pavers 100 are fully loaded with water, the flow rate will immediately increase, then drop back down to become more steady and average at around 1.2 to 2.0 inches per hour. It will be understood that this level of permeability exceeds that required by industry standards.

Experimental Test Results for Permeable Paver 100′

The permeable paver 100′ of the present invention can be manufactured incorporating up to 40% by weight SCM recovered from CO₂ waste flue gas or other sources of waste CO₂ through a process of mineralization of the CO₂ via aqueous precipitation. In an alternate embodiment, the permeable paver comprises 30% SCMs formed by mineralization via aqueous precipitation. Utilization of waste CO₂ to produce SCMs by mineralization via aqueous precipitation will result in a permeable paver 100′ which enables greater compliance with LEED standards. As discussed, such permeable paver 100′ will not only reduce runoff of rain water but result in reduction of carbon emissions by utilizing the CO, commonly found in waste flue gases to produce the SCMs used in the present invention.

Thus, the permeable paver 100′ of the present invention can essentially help lower greenhouse emissions and emissions of CO₂ by using SCM products formed using waste CO₂.

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the present invention belongs. Although any methods and materials similar or equivalent to those described can be used in the practice or testing of the present invention, the preferred methods and materials are now described. All publications and patent documents referenced in the present invention are incorporated herein by reference.

While the principles of the invention have been made clear in illustrative embodiments, there will be immediately obvious to those skilled in the art many modifications of structure, arrangement, proportions, the elements, materials, and components used in the practice of the invention, and otherwise, which are particularly adapted to specific environments and operative requirements without departing from those principles. The appended claims are intended to cover and embrace any and all such modifications, with the limits only of the true purview, spirit and scope of the invention. 

We claim:
 1. A permeable paver formed into a predetermined size and shape utilizing a hydraulic-type compacting block forming machine, the permeable paver comprising (i) a base of 3 parts by weight of blast-furnace slag and 1 part by weight of sand, (ii) between about one fifth and one half part by weight of ¼″ gravel, (iii) between 15 and 21 parts by weight portland cement of which up to 40% comprises SCMs formed by mineralization of CO₂, the paver having a water permeability in excess of 1 inch per hour and having an average compressive strength in excess of about 8000 psi.
 2. The permeable paver of claim 1 wherein 30% of the portland cement is comprised of SCMs formed by mineralization of CO₂.
 3. The permeable paver of claim 1 wherein the SCMs formed by mineralization of CO₂ comprise calcium carbonate recovered by aqueous precipitation.
 4. The permeable paver of claim 1, further comprising spacer bars and/or grooves located peripherally thereon to increase absorption between pavers.
 5. The permeable paver of claim 1, further comprising one or more color agents.
 6. The permeable paver of claim 1, wherein the blast-furnace slag is ground and/or granulated.
 7. The permeable paver of claim 4 in which the blast-furnace slag is pre-processed through an industry standard 3/16″ No. 4 sieve.
 8. A permeable paver formed into a predetermined size and shape utilizing a hydraulic-type compacting block forming machine, the permeable paver comprising (i) a base of 3 parts by weight of blast-furnace slag and 1 part by weight of sand, (ii) between about one fifth and one half part by weight of ¼″ gravel, (iii) between 15 and 21 parts by weight portland cement wherein between about 5 and 7 parts by weight of the portland cement are SCMs containing calcium carbonate formed by mineralization of CO₂, the paver having a water permeability in excess of 1 inch per hour and having an average compressive strength in excess of about 8000 psi. 